If tubes having the tolerances and are produced according to the technical conditions of deivery as specified in this Standard are to e used as pipelines, then the dimensions specified in DIN 2448 may from time to time be used. These tubes must be ordered according to quality grade C.
| Grade | Mfg. Process | Chemical composition
| |||||||||
| C | Si | Mn | P | S | Ni | Cr | Mo | Others | ① | ||
| ② | |||||||||||
| ③ | |||||||||||
| ④ | |||||||||||
| St30Si | S | 0.10Max | 0.30Max | ≤0.55 | 0.040Max | 0.040Max | - | - | - | - | ① |
| ② | |||||||||||
| ③ | |||||||||||
| ④ | |||||||||||
| St30A1 | S | 0.10Max | 0.05Max | ≤0.55 | 0.040Max | 0.040Max | - | - | - | Al deoxydized | ① |
| ② | |||||||||||
| ③ | |||||||||||
| ④ | |||||||||||
| St35 | S | 0.17Max | 0.35Max | ≥0.40 | 0.050Max | 0.050Max | - | - | - | - | ① |
| ② | |||||||||||
| ③ | |||||||||||
| ④ | |||||||||||
| St45 | S | 0.21Max | 0.35Max | ≥0.40 | 0.050Max | 0.050Max | - | - | - | - | ① |
| ② | |||||||||||
| ③ | |||||||||||
| ④ | |||||||||||
| St52 | S | 0.22Max | 0.55Max | ≥1.60 | 0.050Max | 0.050Max | - | - | - | - | ① |
| ② | |||||||||||
| ③ | |||||||||||
| ④ |
①Cold-finished/hard ②Cold-finished/soft ③Annealed ④Normalized
Grade
| Material number | Tensile Test MPa or N/mm2 | Remaks(Similar to JIS) | Possibility Temperature | ||
| Min Yield point | Tensile Strength | ||||
| St30Si | 1.0211 | - | 400Min | (STKM11) | |
| - | 355Min | ||||
| - | 285Min | ||||
| 215 | 295~420 | ||||
| St30Al | 1.0212 | - | 400Min | (STKM11) | |
| - | 355Min | ||||
| - | 285Min | ||||
| 215 | 295~420 | ||||
| St35 | 1.0308 | - | 440Min | (STC38) | |
| - | 370Min | ||||
| - | 315Min | ||||
| 235 | 340~470 | ||||
| St45 | 1.0408 | - | 540Min | (STKM13) | |
| - | 470Min | ||||
| - | 390Min | ||||
| 255 | 440~570 | ||||
| St52 | 1.0580 | - | 590Min | (STKM19) | |
| - | 540Min | ||||
| - | 490Min | ||||
| 350 | 490~630 | ||||